Engineering Plastics Grade Nylon 66 Resin Fiber Greade Nylon 66 Resin Property Specifications of the Modified Nylon 66 Resin
Description Unit Test Standard Condition
Brand
Enhanced Elasticized Enhanced & Elasticized Flame Retardant
2710G 2720G 2130G 2730G 2750G
2103T 2703T 2703TL 2108T 2720E
2107H 2700F
Mechanical Properties        
Tensile Strength MPa ISO527 Dry
90 130 165 170 200
60.3 53.11 51.4 45 48
150
 72.0
Elongation at Break % ISO527 Dry
6.8 6.68 6.6 7.4 6.5
26.2 26.47 39.8 24 24.1
8.4
 5.5
Bending Strength MPa ISO178 Dry
133.2 145.4 212.1 228.7 306.4
64.6 47.97 48.9 60.2 60.1
217.3
 80.1
Bending Modulus GPa ISO178 Dry
2.0 3.55 5.3 5.4 7.9
1.4 1.14 1.2 1.0 1.1
4.5
 2.01
Free Beam IMPact Strength KJ/m2 ISO179 Dry
45 50 50 60 110
unb unb unb unb unb
60
 106.8
Free Beam Notched IMPact Strength KJ/m2 ISO179 Dry
8.5 12 17 17 20
72.8 61.3 57.6 80 20
17
 5.7
Izod Notched IMPact Strength KJ/m2 ISO180 Dry
5.6 9.5 14.8 17.4 19.6
63.9 63.3 52.8 50.5 14.4
17.2
 5.1
Thermal Property        
Melt Flow Velocity g/10min ISO1133 Dry
47.1 17.4 19.5 31.9 18.8
15.8 47.2 7.0 2.4 15.8
15.8
 40.9
Melting Range ℃ ISO3146 Dry
257-262 -- 250-257 254-261 261-270
246-255 253-257 252-265 244-263 245-258
245-258
 253-259
Thermal Deformation Temp. ℃ ISO75 1.80MPa
210 244.6 247.2 248.6 252.9
66.4 73.1 63.4 66.2 69.5
238.5
 74.1
Linear Expansion
Coefficient
 10-5K ISO11359  
-- 2.0-3 1.5-2 1.5-2 0.5-2
80 80 80 -- --
--
 --
Electrical Property        
Volume Resistivity Ω•cm IEC93 Dry
-- -- -- 5.8X1013 --
-- -- -- -- --
--
 8.9X1013
Dielectric Strength Kv/mm IEC243 Dry
-- -- -- 21.0 --
-- -- -- -- --
--
 17.2
Others        
Flammability -- UL94 --
HB HB HB HB HB
-- -- -- -- --
--
 V-0
Density g/cm3 ISO1183 --
-- 1.28 1.36 1.36 1.55
1.12 1.12 1.12 -- --
--
 --
Moulding Shinkage
Parallel
Vertical
%
%
--
--
--
--
0.30 -- 0.05 0.05 0.05
1.10 1.00 1.45 1.20 1.55
--
 0.40
0.85 -- 1.05 1.10 0.35
1.20 1.25 1.60 1.30 1.85
0.75
 0.45
NOTE:Above data is just of typical and only for type selection reference.